Ceramic Fiber Blanket is composed of long flexible, interwoven fibers manufactured by the “spun” process yielding a strong, lightweight, durable product. This material can be used for applications with temperatures from 1000°F (538°C) to 2600°F (1425°C). Blankets have high tensile strength for longer life and durability. Maxwool Ceramic Fiber Blankets contain no binders and are completely inorganic. Thermal and physical properties are retained after drying following wetting by oil, steam or water. This ceramic fiber blanket products are completely inorganic, so there are no fumes when heating for the first time.
Ceramic Fiber Blankets can be used in various applications which include Petrochemical, Refining, Steel, Ceramic, Glass, Fire Protection and Power Generation. This product can be fabricated and shop installed for most applications.
| Classification temperature (℃) | 1140 | 1260 | 1400 | Testing Standards | |||||||||
| Brands | LYGX-112 | LYGX-212 | LYGX-312 | LYGX- 422 | LYGX-512 | – – | |||||||
| Linear shrinkage (%) | 950℃X24h5≤-3 | 1000℃X24h5≤-3 | 1100℃X24h5≤-3 | 1200℃X24h5≤-3 | 1350℃X24h5≤-3 | GB/T17911 | |||||||
| Thermal conductivity(W/mK)(128Kg/m3) | ≤0.153 | YB/T4130 | |||||||||||
| (Average500℃) | |||||||||||||
| Compressive strength(h(thickness 25mm) | ≥0.04 | ≥0.05 | ≥0.04 | ≥0.06 | GB/T17911 | ||||||||
| Bulk dencity (Kg/m3) | 64/96/128/160 | GB/T17911 | |||||||||||
| Chemical composition (%) | Al2O3 (%) | ≥44 | ≥45 | ≥45 | ≥53 | ≥36 | GB/T6900 GB/T4984 | ||||||
| Sio3 (%) | ≥52 | ≥52 | ≥54 | ≥46 | ≥48 | ||||||||
| Zro3 (%) | __ __ | __ | __ _ | __ _ | ≥15 | ||||||||
| Fe2o3 (%) | ≤1.0 | ≤0.8 | ≤0.2 | ≤0.2 | ≤0.1 | ||||||||
| AL2o3 +SiO2 (%) | ≥96 | ≥97 | ≥99 | ≥99 | |||||||||
| AL2o3 +Sio2 (%) | __ __ | __ | __ _ | __ _ | 99 | ||||||||
| Available size (mm/roll) | 3600/7200X610X20/30/50 | __ | |||||||||||
| Packaging | Inside Plastic bag,outside woven bag | Carton | __ | ||||||||||